1.襯布_避免壓延後合膠紗、裁切後合膠紗及胎面膠上、下層沾黏。
2.輸送帶_輸送帶骨架基布。
| 主要產品 | 主要用途 | 主要原料 | 產品種類 |
| 襯布 | 避免壓延後合膠紗、裁切後合膠紗及胎面膠上、下層沾黏。 | PP聚丙烯 | P0, P1, P2 |
| N6, PET | B8, TT | ||
| 輸送帶帆布 | 輸送帶骨架基布 | NN | 100, 150, 200, 250, 300, 400 |
| EP | 100, 150, 200, 250, 300, 400 | ||
| TN | 135, 225, 250, 300 |
Specifications - Liner
|
CLASSIFICATION |
B8 LINER |
PP LINER |
TT LINER |
||||
|
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
||
|
MATERIAL |
UNIT |
N6 420D/1 |
PET 1000D/1 |
PP 400D/1 |
PP 750D/1 |
PET 420D/1 |
PET 1000D/1 |
|
CORD DENSITY |
EPI |
50+/-2 |
28+/-1 |
50+/-2 |
28+/-1 |
50+/-2 |
21+/-1 |
|
TENSILE STRENGTH |
KG/CM |
MIN 39 |
MIN 72 |
MIN 27 |
MIN 27 |
MIN 39 |
MIN 50 |
|
SHRINKAGE @120CX30’ |
% |
MAX 5 |
MAX 1 |
MAX 5 |
MAX 1 |
MAX 5 |
MAX 1 |
|
FABRIC GAUGE |
MM |
0.38+/-0.08 |
0.38+/-0.08 |
0.38+/-0.08 |
|||
|
FABRIC WEIGHT |
G/M2 |
250+/-15 |
195+/-15 |
205+/-15 |
|||
Specifications – Conveyer Ducks
|
DESCRIPTION |
UNIT |
NN100 |
NN150 |
NN200 |
NN250 |
||||
|
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
||
|
CONSTRUCTION |
D/PLY |
840D/1 |
840D/1 |
1260D/1 |
1260D/1 |
1260D/2 |
840D/2 |
126D/2 |
840D/2 |
|
MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
|
CORD DENSITY |
EPI |
48±2 |
19±1 |
45±2 |
16±1 |
34±2 |
14±1 |
36±2 |
16±1 |
|
BREAKING STRENGTH |
KG/CM |
MIN 120 |
MIN 44 |
MIN 170 |
MIN 60 |
MIN 230 |
MIN 60 |
MIN 270 |
MIN 65 |
|
ELONG. AT 10% LOAD |
% |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
|
HOT AIR SHRINKAGE |
% |
MAX 7.0 |
MAX 7.0 |
MAX 7.0 |
MAX 7.0 |
||||
|
FABRIC WEIGHT |
G/S.Q M |
290±20 |
370±25 |
520±25 |
570±30 |
||||
|
FABRIC GAUGE |
MM |
0.45±0.06 |
0.57±0.06 |
0.80±0.08 |
0.85±0.08 |
||||
|
ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
||||
|
DESCRIPTION |
UNIT |
NN300 |
NN400 |
EP100 |
EP125 |
||||
|
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
||
|
CONSTRUCTION |
D/PLY |
1260D/3 |
1260D/2 |
1260D/4 |
1260D/2 |
1000D/1 |
840D/1 |
1500D/1 |
840D/2 |
|
MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
PET |
N66 |
PET |
N66 |
|
CORD DENSITY |
EPI |
30±2 |
11±1 |
32±2 |
11±1 |
49±2 |
19±1 |
40±2 |
14±1 |
|
BREAKING STRENGTH |
KG/CM |
MIN 330 |
MIN 72 |
MIN 460 |
MIN 72 |
MIN 120 |
MIN 45 |
MIN 150 |
MIN 60 |
|
ELONG. AT 10% LOAD |
% |
MAX 3.5 |
-- |
MAX 4.0 |
-- |
MAX 2.5 |
-- |
MAX 2.5 |
-- |
|
HOT AIR SHRINKAGE |
% |
MAX 7.0 |
MAX 8.0 |
MAX 5.0 |
MAX 5.0 |
||||
|
FABRIC WEIGHT |
G/S.Q M |
700±30 |
920±40 |
360±25 |
440±25 |
||||
|
FABRIC GAUGE |
MM |
1.03±0.10 |
1.35±0.15 |
0.47±0.05 |
0.61±0.06 |
||||
|
ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
||||
|
DESCRIPTION |
UNIT |
EP150 |
EP200 |
EP300 |
EP400 |
||||
|
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
||
|
CONSTRUCTION |
D/PLY |
1000D/2 |
840D/2 |
1000D/3 |
840D/2 |
1000D/4 |
840D/4 |
1500D/3 |
1260D/3 |
|
MATERIAL |
|
PET |
N66 |
PET |
N66 |
PET |
N66 |
PET |
N66 |
|
CORD DENSITY |
EPI |
35±2 |
15±1 |
31±2 |
15±1 |
36±2 |
10±1 |
39±2 |
8±1 |
|
BREAKING STRENGTH |
KG/CM |
MIN 170 |
MIN 60 |
MIN 220 |
MIN 60 |
MIN 340 |
MIN 85 |
MIN 450 |
MIN 85 |
|
ELONG. AT 10% LOAD |
% |
MAX 2.5 |
-- |
MAX 2.5 |
-- |
MAX 3.0 |
-- |
MAX 3.0 |
-- |
|
HOT AIR SHRINKAGE |
% |
MAX 5.0 |
MAX 5.0 |
MAX 5.0 |
MAX 5.0 |
||||
|
FABRIC WEIGHT |
G/S.Q M |
500±25 |
605±25 |
935±30 |
1060±40 |
||||
|
FABRIC GAUGE |
MM |
0.67±0.08 |
0.78±0.09 |
1.10±0.11 |
1.30±0.15 |
||||
|
ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
||||