以人造纖維、合成纖維原絲進行撚絲、織布與浸漬後，為輸送帶骨架基布材質。
| 主要產品 | 主要用途 | 主要原料 | 產品種類 |
| 輸送帶帆布 | 用於輸送帶產品，提供輸送帶尺寸穩定性、強度、剛性以及耐久性。依經紗整片強度Kg/cm為等級標準 | NN（Nylon 6） | NN 100；NN 150；NN 200；NN 250；NN 300；NN 400 |
| EP（Polyester+Nylon 66） | EP 100；EP 150；EP 200；EP 250；EP 300；EP 400 |
|
Description |
Unit |
EP100 |
EP125 |
EP150 |
EP200 |
EP250 |
EP300 |
EP350 |
NN400 |
||||||||
|
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
||
|
Breaking Strength |
Kg/cm |
Min 120 |
Min 45 |
Min 150 |
Min 60 |
Min 170 |
Min 60 |
Min 220 |
Min 60 |
Min 270 |
Min 85 |
Min 340 |
Min 85 |
Min 380 |
Min 85 |
Min 450 |
Min 85 |
|
Elongation At 10% Load |
% |
Max 2.5 |
─ |
Max 2.5 |
─ |
Max 2.5 |
─ |
Max 2.5 |
─ |
Max 3.0 |
─ |
Max 3.0 |
─ |
Max 3.0 |
─ |
Max 3.0 |
─ |
|
Hot Air Shrinkage |
% |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
Max 5.0 |
─ |
|
Fabric Gauge |
mm |
0.47±0.05 |
0.61±0.06 |
0.67±0.08 |
0.78±0.09 |
1.10±0.10 |
1.10±0.10 |
1.30±0.10 |
1.30±0.15 |
||||||||
|
Unit Weight |
g/m2 |
360±25 |
440±25 |
500±25 |
605±25 |
745±30 |
935±30 |
1000±40 |
1060±40 |
||||||||
|
Adhesion Peel test |
Kg/cm |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
||||||||
|
Description |
Unit |
NN100 |
NN150 |
NN200 |
NN250 |
NN300 |
NN400 |
||||||
|
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
Warp |
Weft |
||
|
Breaking Strength |
Kg/cm |
Min 120 |
Min 44 |
Min 170 |
Min 60 |
Min 230 |
Min 60 |
Min 270 |
Min 65 |
Min 330 |
Min 72 |
Min 460 |
Min 72 |
|
Elongation At 10% Load |
% |
Max 4.5 |
─ |
Max 4.5 |
─ |
Max 4.5 |
─ |
Max 4.5 |
─ |
Max 4.5 |
─ |
Max 4.5 |
─ |
|
Hot Air Shrinkage |
% |
Max 7.0 |
─ |
Max 7.0 |
─ |
Max 7.0 |
─ |
Max 7.0 |
─ |
Max 7.0 |
─ |
Max 8.0 |
─ |
|
Fabric Gauge |
mm |
0.45±0.06 |
0.57±0.06 |
0.80±0.08 |
0.85±0.08 |
1.05±0.10 |
1.35±0.15 |
||||||
|
Unit Weight |
g/m2 |
290±25 |
370±25 |
520±25 |
570±30 |
700±30 |
920±40 |
||||||
|
Adhesion Peel test |
Kg/cm |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
Min 12.0 |
||||||