Tyre Cord Plant
We produce tire cord, chafer, and conveyor ducks.
Our tire cord plant is a renowned manufacturer in the world with the capacity of 3,600 tons per month.
The main processes are twisting, weaving, dipping and packing.
We use the latest machinery and experiment equipment from Germany, France, Switzerland and Japan to strictly ensure its product quality.
Our products have been promoted to the famous tire manufacturers in Asia-pacific and other areas, and have got ISO certificate. Besides,
Our products are very reliable to our customers.
| Main Product | Main Usage |
Raw Material | Product Items |
| Tyre Cord | Fabrics Tyre cord fabrics for bicycles, motocycles, passenger cars,trucks, mobile cranes. |
nylon 6 | 210D/1, 420D/1, 630D/1840D/1, D/2, 1260D/1, D/2, D/3, 1680D/2, 1890D/2 |
| nylon 66 | 840D/1, D/2, 1260D/1, D/2, D/3, 1680D/2, 1890D/2 |
| polyester | 1000D/2, 1000D/3, 1500D/2R-Type, HMLS-Type. |
| Chafer Fabrics | Chafers for tyre-lips |
nylon 6 | Multi 420D/1, 840D/1, 1260D/1 Mono 420D/1, Mono Multi 420D/1 |
| nylon 66 | Mono 420D/1, Mono Multi 420D/1 |
| Conveyor Ducks | Lining canvas or ducks for conveyor belts. |
NN | 100,150,200,250,300,400 |
| EP | 100,150,200,250,300,400 |
| TN | 135,225,250,300 |
Contact:
Taipei: Mr. David Wang / u030504@ftc.com.tw Tel: +886-2-8770-1712 Fax: +886-2-2717-1158
Touliu: Mr. H.C. TSAI/ u046949@ftc.com.tw Tel: +886-5-557-7397; Fax:+886-5-557-3574
Specifications - Dipped Tire Cords
| CLASSIFICATION |
NYLON 6 DIPPED TIRE CORD |
| DESCRIPTION |
UNIT |
840D/2
940DTEX/2 |
1260D/2
1400DTEX/2 |
1680D/2
1880DTEX/2 |
1260D/3
1400DTEX/3 |
1890D/2
2100DTEX/2 |
| TWIST PLY, Z |
T/M |
470กำ20 |
380กำ20 |
330กำ20 |
310กำ20 |
310กำ20 |
| TWIST CABLE, S |
T/M |
460กำ20 |
370กำ20 |
320กำ20 |
300กำ20 |
300กำ20 |
| BREAKING STRENGTH |
KG |
MIN 13.5 |
MIN 21.0 |
MIN 27.5 |
MIN 30.5 |
MIN 31.0 |
| ELONGATION AT BREAK |
% |
26กำ4 |
26กำ4 |
26กำ4 |
26กำ4 |
26กำ4 |
| EASL |
% |
9.5กำ2.0 |
9.5กำ2.0 |
9.5กำ2.0 |
9.5กำ2.0 |
9.5กำ2.0 |
| HOT AIR SHRINKAGE |
% |
MAX 6.0 |
MAX 6.0 |
MAX 6.0 |
MAX 6.0 |
MAX 6.0 |
| CORD GAUGE |
% |
0.55กำ0.03 |
0.66กำ0.03 |
0.76กำ0.03 |
0.82กำ0.03 |
0.82กำ0.03 |
| ADHESION H-TEST, PER 10MM EMBEDDMENT |
KG |
MIN 11.0 |
MIN 16.0 |
MIN 17.0 |
MIN 17.0 |
MIN 17.0 |
| CLASSIFICATION |
NYLON 6 DIPPED TIRE CORD |
| DESCRIPTION |
UNIT |
210D/1
235DTEX/1 |
420D/1
470DTEX/1 |
630D/1
700DTEX/1 |
840D/1
940DTEX/1 |
1260D/1
1400DTEX/1 |
| TWIST PLY, S |
T/M |
280กำ15 |
280กำ15 |
280กำ15 |
280กำ15 |
250กำ15 |
| BREAKING STRENGTH |
KG |
MIN 1.50 |
MIN 3.40 |
MIN 5.10 |
MIN 7.00 |
MIN 10.5 |
| ELONGATION AT BREAK |
% |
22กำ4 |
22กำ4 |
22กำ4 |
23กำ4 |
23กำ4 |
| EASL |
% |
11.5กำ2.0 |
11.5กำ2.0 |
11.5กำ2.0 |
12.0กำ2.0 |
12.0กำ2.0 |
| HOT AIR SHRINKAGE |
% |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
| CORD GAUGE |
% |
0.13กำ0.02 |
0.25กำ0.03 |
0.28กำ0.03 |
0.35กำ0.03 |
0.42กำ0.03 |
| ADHESION HOT U-TEST |
KG |
MIN 1.0 |
MIN 2.5 |
MIN 4.0 |
MIN 5.0 |
MIN 8.0 |
| CLASSIFICATION |
NYLON 66 DIPPED TIRE CORD |
| DESCRIPTION |
UNIT |
840D/2
940DTEX/2 |
1260D/2
1400DTEX/2 |
1680D/2
1880DTEX/2 |
1260D/3
1400DTEX/3 |
1890D/2
2100DTEX/2 |
| TWIST PLY, Z |
T/M |
470กำ20 |
380กำ20 |
330กำ20 |
310กำ20 |
310กำ20 |
| TWIST CABLE, S |
T/M |
460กำ20 |
370กำ20 |
320กำ20 |
300กำ20 |
300กำ20 |
| BREAKING STRENGTH |
KG |
MIN 14.0 |
MIN 21.0 |
MIN 27.5 |
MIN 30.5 |
MIN 31.0 |
| ELONGATION AT BREAK |
% |
23กำ4 |
23กำ4 |
23กำ4 |
23กำ4 |
23กำ4 |
| EASL |
% |
9.0กำ2.0 |
9.0กำ2.0 |
9.0กำ2.0 |
9.0กำ2.0 |
9.0กำ2.0 |
| HOT AIR SHRINKAGE |
% |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
MAX 4.5 |
| CORD GAUGE |
% |
0.55กำ0.03 |
0.66กำ0.03 |
0.76กำ0.03 |
0.82กำ0.03 |
0.82กำ0.03 |
| ADHESION H-TEST, PER 10MM EMBEDDMENT |
KG |
MIN 11.0 |
MIN 16.0 |
MIN 17.0 |
MIN 17.0 |
MIN 17.0 |
| CLASSIFICATION |
NYLON 66 DIPPED TIRE CORD |
| DESCRIPTION |
UNIT |
420D/1
470DTEX/1 |
840D/1
940DTEX/1 |
1260D/1
1400DTEX/1 |
| TWIST PLY, S |
T/M |
280กำ15 |
280กำ15 |
250กำ15 |
| BREAKING STRENGTH |
KG |
MIN 3.40 |
MIN 7.00 |
MIN 10.5 |
| ELONGATION AT BREAK |
% |
21กำ4 |
21กำ4 |
21กำ4 |
| EASL |
% |
11.0กำ2.0 |
11.0กำ2.0 |
11.0กำ2.0 |
| HOT AIR SHRINKAGE |
% |
MAX 3.0 |
MAX 3.0 |
MAX 3.0 |
| CORD GAUGE |
% |
0.25กำ0.03 |
0.35กำ0.03 |
0.42กำ0.03 |
| ADHESION HOT U-TEST |
KG |
MIN 2.5 |
MIN 5.0 |
MIN 8.0 |
| CLASSIFICATION |
DIPPED TIRE CORD - POLYESTER DSP TYPE |
| DESCRIPTION |
UNIT |
1000D/2
1100DTEX/2 |
1000D/3
1100DTEX/3 |
1500D/2
1670DTEX/2 |
1300D/2
1440DTEX/2 |
| TWIST PLY, Z |
T/M |
470กำ20 |
400กำ20 |
400กำ20 |
390กำ20 |
| TWIST CABLE, S |
T/M |
460กำ20 |
400กำ20 |
400กำ20 |
390กำ20 |
| BREAKING STRENGTH |
KG |
MIN 13.5 |
MIN 19.5 |
MIN 20.0 |
MIN 18.0 |
| ELONGATION AT BREAK |
% |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
| EASL |
% |
4.5กำ1.0 |
4.5กำ1.0 |
4.5กำ1.0 |
4.5กำ1.0 |
| HOT AIR SHRINKAGE |
% |
MAX 3.5 |
MAX 3.5 |
MAX 3.5 |
MAX 3.5 |
| CORD GAUGE |
% |
0.58กำ0.03 |
0.68กำ0.03 |
0.68กำ0.03 |
0.63กำ0.03 |
| ADHESION H-TEST, PER 10MM EMBEDDMENT |
KG |
MIN 11.0 |
MIN 13.0 |
MIN 13.0 |
MIN 12.0 |
TEST METHOD:
1. ALL TEST ITEMS TESTED ACCORDING TO ASTM D885-85 EXCEPT ADHESION H-TEST / HOT U-TEST.
2. BREAKING STRENGTH, ELONGATION AT BREAK & EASL (ELONGATION AT SPECIFIED LOAD) TESTED BY CONDITIONED METHOD.
3. ADHESION H-TEST TESTED ACCORDING TO ASTM D2138-83.
Specifications - Chafer
| CLASSIFICATION |
MONO 420D/1 |
MONO 420D/1 |
MONO 420D/1 |
MONO 420D/1 |
| WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WART |
WEFT |
| MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
N66 |
N66 |
N66 |
N66 |
| CORD DENSITY |
EPI |
23+/-1.5 |
23+/-1.5 |
20+/-1.5 |
20+/-1.5 |
23+/-1.5 |
23+/-1.5 |
20+/-1.5 |
20+/-1.5 |
| TENSILE STRENGTH |
KG/CM |
MIN 20 |
MIN 19 |
MIN 19 |
MIN 18 |
MIN 20 |
MIN 19 |
MIN 19 |
MIN 18 |
| BREAK ELONG. (REF) |
% |
17 |
25 |
17 |
25 |
16 |
23 |
16 |
23 |
| HOT AIR SHRINKAGE |
% |
Max 4.5 |
Max 1.8 |
Max 4.5 |
Max 1.8 |
Max 3.5 |
Max 1.5 |
Max 3.5 |
Max 1.5 |
| UNIT WEIGHT |
G/M2 |
95+/-10 |
85+/-10 |
95+/-10 |
85+/-10 |
| ADHESION BY STRIP |
KG/IN |
Min 17 |
Min 15 |
Min 17 |
Min 15 |
| CLASSIFICATION |
840D/1 |
1260D/1 |
| WARP |
WEFT |
WART |
WEFT |
| MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
| CORD DENSITY |
EPI |
17+/-1 |
17+/-1 |
16+/-1 |
16+/-1 |
| TENSILE STRENGTH |
KG/CM |
Min 40 |
Min 38 |
Min 58 |
Min 55 |
| BREAK ELONG. (REF) |
% |
20 |
33 |
20 |
33 |
| HOT AIR SHRINKAGE |
% |
Max 4.5 |
Max 2 |
Max 4.5 |
Max 2 |
| UNIT WEIGHT |
G/M2 |
155+/-15 |
225+/-20 |
| ADHESION BY STRIP |
KG/IN |
Min 17 |
Min 17 |
Specifications - Liner
| CLASSIFICATION |
B8 LINER |
PP LINER |
TT LINER |
| WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
| MATERIAL |
|
N6 420D/1 |
PET 1000D/1 |
PP 400D/1 |
PP 750D/1 |
PET 420D/1 |
PET 1000D/1 |
| CORD DENSITY |
EPI |
50+/-2 |
28+/-1 |
50+/-2 |
28+/-1 |
50+/-2 |
21+/-1 |
| TENSILE STRENGTH |
KG/CM |
MIN 39 |
MIN 72 |
MIN 27 |
MIN 27 |
MIN 39 |
MIN 50 |
| SHRINKAGE @120CX30กฆ |
% |
MAX 5 |
MAX 1 |
MAX 5 |
MAX 1 |
MAX 5 |
MAX 1 |
| FABRIC GAUGE |
MM |
0.38+/-0.08 |
0.38+/-0.08 |
0.38+/-0.08 |
| FABRIC WEIGHT |
G/M2 |
250+/-15 |
195+/-15 |
205+/-15 |
Specifications - Conveyer Ducks
| DESCRIPTION |
UNIT |
NN100 |
NN150 |
NN200 |
NN250 |
| WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
| CONSTRUCTION |
D/PLY |
840D/1 |
840D/1 |
1260D/1 |
1260D/1 |
1260D/2 |
840D/2 |
126D/2 |
840D/2 |
| MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
N6 |
| CORD DENSITY |
EPI |
48กำ2 |
19กำ1 |
45กำ2 |
16กำ1 |
34กำ2 |
14กำ1 |
36กำ2 |
16กำ1 |
| BREAKING STRENGTH |
KG/CM |
MIN 120 |
MIN 44 |
MIN 170 |
MIN 60 |
MIN 230 |
MIN 60 |
MIN 270 |
MIN 65 |
| ELONG. AT 10% LOAD |
% |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
MAX 3.5 |
-- |
| HOT AIR SHRINKAGE |
% |
MAX 7.0 |
MAX 7.0 |
MAX 7.0 |
MAX 7.0 |
| FABRIC WEIGHT |
G/S.Q M |
290กำ20 |
370กำ25 |
520กำ25 |
570กำ30 |
| FABRIC GAUGE |
MM |
0.45กำ0.06 |
0.57กำ0.06 |
0.80กำ0.08 |
0.85กำ0.08 |
| ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
| DESCRIPTION |
UNIT |
NN300 |
NN400 |
EP100 |
EP125 |
| WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
| CONSTRUCTION |
D/PLY |
1260D/3 |
1260D/2 |
1260D/4 |
1260D/2 |
1000D/1 |
840D/1 |
1500D/1 |
840D/2 |
| MATERIAL |
|
N6 |
N6 |
N6 |
N6 |
PET |
N66 |
PET |
N66 |
| CORD DENSITY |
EPI |
30กำ2 |
11กำ1 |
32กำ2 |
11กำ1 |
49กำ2 |
19กำ1 |
40กำ2 |
14กำ1 |
| BREAKING STRENGTH |
KG/CM |
MIN 330 |
MIN 72 |
MIN 460 |
MIN 72 |
MIN 120 |
MIN 45 |
MIN 150 |
MIN 60 |
| ELONG. AT 10% LOAD |
% |
MAX 3.5 |
-- |
MAX 4.0 |
-- |
MAX 2.5 |
-- |
MAX 2.5 |
-- |
| HOT AIR SHRINKAGE |
% |
MAX 7.0 |
MAX 8.0 |
MAX 5.0 |
MAX 5.0 |
| FABRIC WEIGHT |
G/S.Q M |
700กำ30 |
920กำ40 |
360กำ25 |
440กำ25 |
| FABRIC GAUGE |
MM |
1.03กำ0.10 |
1.35กำ0.15 |
0.47กำ0.05 |
0.61กำ0.06 |
| ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
| DESCRIPTION |
UNIT |
EP150 |
EP200 |
EP300 |
EP400 |
| WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
WARP |
WEFT |
| CONSTRUCTION |
D/PLY |
1000D/2 |
840D/2 |
1000D/3 |
840D/2 |
1000D/4 |
840D/4 |
1500D/3 |
1260D/3 |
| MATERIAL |
|
PET |
N66 |
PET |
N66 |
PET |
N66 |
PET |
N66 |
| CORD DENSITY |
EPI |
35กำ2 |
15กำ1 |
31กำ2 |
15กำ1 |
36กำ2 |
10กำ1 |
39กำ2 |
8กำ1 |
| BREAKING STRENGTH |
KG/CM |
MIN 170 |
MIN 60 |
MIN 220 |
MIN 60 |
MIN 340 |
MIN 85 |
MIN 450 |
MIN 85 |
| ELONG. AT 10% LOAD |
% |
MAX 2.5 |
-- |
MAX 2.5 |
-- |
MAX 3.0 |
-- |
MAX 3.0 |
-- |
| HOT AIR SHRINKAGE |
% |
MAX 5.0 |
MAX 5.0 |
MAX 5.0 |
MAX 5.0 |
| FABRIC WEIGHT |
G/S.Q M |
500กำ25 |
605กำ25 |
935กำ30 |
1060กำ40 |
| FABRIC GAUGE |
MM |
0.67กำ0.08 |
0.78กำ0.09 |
1.10กำ0.11 |
1.30กำ0.15 |
| ADHESION BY STRIP |
KG/CM |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
MIN 12.0 |
|